Transparent Non Heat Sealable both side corona treated
HIGH TREATED OPP LAYER
OPP CORE LAYER
TREATED OPP LAYER
Description
Transparent Non Heat Sealable both side corona treated Film
Features
Great Lamination Bond
Excellent Optics & haze
Good Machinability
Good Ink Adhesion
Application
LAMINATION
THE BIG DIFFERENTIATORS
01
Good Ink Adhesion
Excellent print quality capability
02
Good Wet Lamination Adhesive Bond
Offers strong fiber-tear adhesion, contributing to a sophisticated brand image.
03
Superior print quality
Consistent half-tone dot transfer.
04
Differential Treatment
No ink transfer & clear batch coding.
05
Excellent processing performance
High-efficiency performance with minimal waste.
PROPERTIES
TEST METHOD (ASTM)
UNIT
TYPICAL VALUES
TPL-08
TPL-09
TPL-10
TPL-12
TPL-15
PHYSICAL
Thickness
ASTM D 374
MICRON
08
09
10
12
15
Grammage
NTM
gm/m²
7.28
8.2
9.1
10.9
13.6
Yield
NTM
m²/kg
137.3
122.1
109.9
91.6
73.2
Thickness variation
%(±)
3
3
3
3
3
SURFACE
Treatment Level (min)
ASTM D 2578
dyne/cm
38
38
38
38
38
OPTICAL
Haze
ASTM D 1003
%
1.0-1.50
1.0-1.50
1.0-1.50
1.0-1.50
1.0-1.50
Gloss
ASTM D 2457
-
90-95
90-95
90-95
90-95
90-95
MECHANICAL
Coefficient Of Friction
ASTM D 1894
Static
Kinetic
0.40-0.45
0.40-0.45
0.40-0.45
0.40-0.45
0.40-0.45
0.30-0.35
0.30-0.35
0.30-0.35
0.30-0.35
0.30-0.35
Tensile Strength
MD
TD
ASTM D 882
kg/cm²
≥ 1200
≥ 1200
≥ 1200
≥ 1200
≥ 1200
≥ 2400
≥ 2400
≥ 2400
≥ 2400
≥ 2400
Modulus
MD
TD
ASTM D 882
kg/cm²
≥ 16000
≥ 16000
≥ 16000
≥ 16000
≥ 16000
≥ 26000
≥ 26000
≥ 26000
≥ 26000
≥ 26000
Elongation
MD
TD
ASTM D 882
%
140-160
140-160
140-160
140-160
140-160
40-60
40-60
40-60
40-60
40-60
THERMAL
Shrinkage at 120°C/5min
MD
TD
ASTM D 1204
%
3.0-5.0
3.0-5.0
3.0-5.0
3.0-5.0
3.0-5.0
1.0-3.0
1.0-3.0
1.0-3.0
1.0-3.0
1.0-3.0
BARRIER
Water Vapour Transmission Rate
ASTM F 1249
gm/m²/24h
8.5
8.5
8.0
8.0
7.5
Oxygen Gas Transmission Rate
ASTM D 3985
cc/m²/24h
2500
2500
2400
2400
2300
STORAGE & HANDLING
NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. Material should be use before 3 months from dispatch
FOOD CONTACT
NAHAROPP™ Follow with EU and FDA regulations. MSDS are available on customer request.
DISCLAIMER
The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its
own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor
accept any responsibility for the fitness of the product for any other use. Post-consumer recycled material is not used.
NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION