Specific Applications Film

HTC

TRANSPARENT BOTH SIDE HEAT SEALABLE BOTH SIDE CORONA TREATED

 
tds

TREATED SEALABLE LAYER

OPP CORE LAYER

TREATED SEALABLE LAYER

t6s
Description

 TRANSPARENT BOTH SIDE HEAT SEALABLE BOTH SIDE CORONA TREATED FILM

Features
  • Excellent Machinability
  • Good Heat Seal
  • Balance Slip
  • Good Antistatic
  • Joint Less 
Application

 CABLE OVERWRAP

 

PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
HTC-20 HTC-25
PHYSICAL
Thickness ASTM D 374 MICRON
20 25
Grammage NTM gm/m²
18.2 22.8
Yield NTM m²/kg
55.0 44.0
Thickness variation %(±) 3
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm 38
OPTICAL
Haze
ASTM D 1003

%

2.0-2.80

Gloss
ASTM D 2457

-

85-90

MECHANICAL
Coefficient Of Friction ASTM D 1894

Static

Kinetic

0.30

0.25

Tensile Strength

MD

TD

ASTM D 882

kg/cm²

1200-1700

2500-2800

Modulus

MD

TD

ASTM D 882

kg/cm²

16000-19000

26000-29000

Elongation

MD

TD

ASTM D 882

%

140-180

40-80

THERMAL
Shrinkage at 120°C/5min

MD

TD

ASTM D 1204

%

3.0-5.0

1.0-3.0

Seal Initiation Temperature (Max)

NTM

°C

112-115

Sealing Strength (min) at 120ºC/2Bar

NTM

gms/25mm

400-500

DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION