150x50
 

Specific Applications Film

HAF

TRANSPARENT HEAT SEALABLE ANTI FOG BOTH SIDE CORONA TREATED

 
tds

TREATED SEALABLE LAYER WITH ANTI-FOG

INTER LAYER

OPP CORE LAYER

INTER LAYER

TREATED HEAT SEALABLE LAYER

t6s
Description

Tranparent heat Sealable anti-fog both side corona Treated Film-Excellent Cold and Hot Antifog effect on one side and other side printable

Features
  • Excellent anti-fog Properties
  • Good Optics
  • Good Sealing Properties
  • Good Machinability 
Application

 FRESH PRODUCTS TO BE KEPT UNDER REFRIGERATION OR ELEVATED TEMPERATURE

THE BIG DIFFERENTIATORS

01

Excellent Anti-fog Performance

Excellent cold and hot antifogging effect on one side and printability on other side

02

Excellent Optics

Finer Print images.

03

Super product visibility

Antimist prevents condensation and ensure excellent product visibility.

04

Excellent Sealing property

Excellent heat seal & hot tack strength

05

Very good machinability

Excellent runnability.

PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
HAF-25 HAF-30 HAF-35 HAF-40
PHYSICAL
Thickness ASTM D 374 MICRON
25 30 35 40
Grammage NTM gm/m²
22.8 27.3 31.8 36.4
Yield NTM m²/kg
44.0 36.6 31.4 27.4
Thickness variation %(±) 3
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm 38
OPTICAL
Haze
ASTM D 1003

%

2.0-3.0

Gloss
ASTM D 2457

-

85-90

MECHANICAL
Coefficient Of Friction ASTM D 1894

FILM/FILM

0.20-0.30

Tensile Strength

MD

TD

ASTM D 882

kg/cm²

1200-1700

2500-2800

Modulus

MD

TD

ASTM D 882

kg/cm²

16000-19000

26000-29000

Elongation

MD

TD

ASTM D 882

%

140-180

40-80

THERMAL
Shrinkage at 120°C/5min

MD

TD

ASTM D 1204

%

3.0-5.0

1.0-3.0

Seal Initiation Temperature (Max)

NTM

°C

118-122

Sealing Strength (min) at 120ºC/2Bar

NTM

gms/25mm

400-500

BARRIER
Water Vapour Transmission Rate ASTM F 1249 gm/m²/24h
6.5 6.0 5.5 5.5
Oxygen Gas Transmission Rate ASTM D 3985 cc/m²/24h
2150 1800 1600 1400
ANTIMIST
Antifog Test NTM Rating A to E
E E E E
STORAGE & HANDLING

NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. material should be use before 3 months from dispatch

FOOD CONTACT

NAHAROPP™ Follow with EC and FDA regulations. MSDS are available on customer request.

DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION

Updated on : 10 March 2022