150x50
 

Specific Applications Film

TML

ONE SIDE MATTE OTHER SIDE GLOSSY CORONA TREATED WITH HS

 
tds

UN-TREATED MATTE OPP LAYER

OPP CORE LAYER

TREATED GLOSSY HS OPP LAYER

t6s
Description

 ONE SIDE MATTE OTHER SIDE GLOSSY CORONA TREATED WITH HS FILM

Features
  • Suitable For Thermal Lamination
  • Excellent Matte Dispersion
  • Good Optics
  • High Haze & Low Gloss
  • Good Heat Seal Property
Application

 EXTRUSION COATING -Base Film For Thermal Lamination Film

PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
TML-12
PHYSICAL
Thickness ASTM D 374 MICRON
12
Grammage NTM gm/m²
10.4
Yield NTM m²/kg
95.8
Thickness variation %(±) 3
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm 38
OPTICAL
Haze
ASTM D 1003

%

75-80

Gloss

Glossy

Matte

ASTM D 2457

-

55-60

10-12

MECHANICAL
Coefficient Of Friction ASTM D 1894

Static

Kinetic

0.55-0.65

0.50-0.60

Tensile Strength

MD

TD

ASTM D 882

kg/cm²

1000-1400

2000-2200

Modulus

MD

TD

ASTM D 882

kg/cm²

14000-17000

24000-28000

Elongation

MD

TD

ASTM D 882

%

140-160

40-60

THERMAL
Shrinkage at 120°C/5min

MD

TD

ASTM D 1204

%

3.0-6.0

1.0-3.0

Seal Initiation Temperature (Max)

NTM

°C

100-105

Sealing Strength (min) at 120ºC/2Bar

NTM

gms/25mm

250-300

BARRIER
Water Vapour Transmission Rate ASTM F 1249 gm/m²/24h
≤8.2
Oxygen Gas Transmission Rate ASTM D 3985 cc/m²/24h
2100
DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION