150x50
 

Labelling Film

HPLT

SUPER WHITE CAVITATED, BOTH SIDE HS BOTH SIDE CORONA TREATED FILM

 
tds

HIGH ENERGY TREATED HS SKIN LAYER

MODIFIED INNER SKIN LAYER

MODIFIED WHITE CAVIATED CORE LAYER

MODIFIED INNER SKIN LAYER

TREATED HS SKIN LAYER

t6s
Description

 SUPER WHITE CAVITATED, BOTH SIDE HS BOTH SIDE CORONA TREATED FILM

Features
  • Excellent pearl white Appearance.
  • Excellent opacity.
  • Excellent machinability.
  • Excellent hot tack properties.
  • Superb gloss.
Application

 Wrap Around and pressure sensitive label application.

THE BIG DIFFERENTIATORS

01

Very good Pearl-White effect

Brilliant pearlescent white Appearance.

02

Superb Gloss

Imparting subtle richness to branding.

03

Good Antistatic

Good Machinability.

04

Good Sealing Functionality

Very good Heat-Seal & Hot-Tack Properties.

05

Very Good Printability

Excellent Encourage of Inks on high Energy Treated side.

PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
HPLT-30 HPLT-35 HPLT-38 HPLT-40
PHYSICAL
Thickness ASTM D 374 MICRON
30 35 38 40
Grammage NTM gm/m²
20.10 23.45 25.46 26.80
Yield NTM m²/kg
49.75 42.64 39.28 37.31
Thickness variation %(±) 5
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm 38
OPTICAL
Transmittance
ASTM D 1003

%

30-40

Gloss
ASTM D 2457

-

70-80

MECHANICAL
Coefficient Of Friction ASTM D 1894

Static

Kinetic

0.40

0.35

Tensile Strength

MD

TD

ASTM D 882

kg/cm²

500-650

1200-1350

Modulus

MD

TD

Elongation

MD

TD

ASTM D 882

%

130

30

THERMAL
Shrinkage at 120°C/5min

MD

TD

ASTM D 1204

%

3.0-3.5

1.5-2.0

Seal Initiation Temperature (Max)

NTM

°C

115-118

Sealing Strength (min) at 120ºC/2Bar

NTM

gms/25mm

300-350

BARRIER
Water Vapour Transmission Rate ASTM F 1249 gm/m²/24h
3.5 3.5 3.5 3.5
Oxygen Gas Transmission Rate ASTM D 3985 cc/m²/24h
1500 1500 1500 1500
STORAGE & HANDLING

NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. material should be use before 3 months from dispatch

FOOD CONTACT

NAHAROPP™ Follow with EC and FDA regulations. MSDS are available on customer request.

DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION

Updated on : 31 March 2023