Lamination Film

MLHS

ONE SIDE METALLISED OTHER SIDE LOW HEAT SEALABLE FILM

 
tds

VACUUM DEPOSITED ALUMINIUM LAYER

METAL RECEPTIVE LAYER

INTER LAYER

OPP CORE LAYER

INTER LAYER

UNTREATED LOW HS LAYER

t6s
Description
ONE SIDE METALLISED OTHER SIDE LOW HEAT SEALABLE FILM

 

Features
  • Outstanding metal appearance. 
  • Excellent metal adhesion.
  • Very good barrier property.
  • Broad Seal range.
  • Very good Heat seal strength.
  • Very good bond strength with SIT 
Application

 Packaging & conversion

THE BIG DIFFERENTIATORS

01

Excellent OTR & WVTR

Improves shelf life of chips, snacks & confectionary. Very good barrier to moisture & Light

02

Extended Seal Functionality

Very low SIT, Excellent HOT-TACK & heat Seal Strength & good bond strength with SIT

03

Exceptional Metal Gloss

Very Good Graphics & Images.

04

Optimal COF

Excellent runnability at high speed m/c & lamination process.

05

Good Metal Bond.

Excellent Durability & sustainability of barrier under extreme conditions.

PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
MLHS-15 MLHS-18 MLHS-20 MLHS-25
PHYSICAL
Thickness ASTM D 374 MICRON
15 18 20 25
Grammage NTM gm/m²
13.6 16.4 18.2 22.8
Yield NTM m²/kg
73.3 61.0 55.0 44.0
Thickness variation %(±) 3
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm 38
OPTICAL
OPTICAL DENSITY
NTM

-

2.0-2.2

MECHANICAL
Coefficient Of Friction ASTM D 1894

Static

Kinetic

0.40-0.45

0.35-0.40

Tensile Strength

MD

TD

ASTM D 882

kg/cm²

1200-1500

2600-3000

Modulus

MD

TD

ASTM D 882

kg/cm²

16000-18000

26000-28000

Elongation

MD

TD

ASTM D 882

%

140-180

40-80

THERMAL
Shrinkage at 120°C/5min

MD

TD

ASTM D 1204

%

3.0-5.0

1.0-3.0

Seal Initiation Temperature (Max)

NTM

°C

105 (Min Bond Strength 150 Gms/25 mm)

Sealing Strength (min) at 120ºC/2Bar

NTM

gms/25mm

400

BARRIER
Water Vapour Transmission Rate ASTM F 1249 gm/m²/24h
0.30 0.30 0.30 0.30
Oxygen Gas Transmission Rate ASTM D 3985 cc/m²/24h
50 50 50 50
STORAGE & HANDLING

NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. material should be use before 3 months from dispatch

FOOD CONTACT

NAHAROPP™ Follow with EC and FDA regulations. MSDS are available on customer request.

DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION