Both Side Heat Sealable ,One Side Glossy Other Side Matte(High COF) Film
UN-TREATED, HEAT SEALABLE MATTE OPP LAYER
INTER LAYER
OPP CORE LAYER
INTER LAYER
TREATED, HEAT SEALABLE GLOSSY OPP LAYER
Description
Both Side Heat Sealable ,One Side Glossy Other Side Matte(High COF) Film
Features
Consistent high COF (>0.60) matt surface
Good matt dispersion
High haze & low gloss
Good printability
Good Machinability
Application
Heavy-duty bags
Big pouch
Rice bags
Pet food
THE BIG DIFFERENTIATORS
01
Consistently High COF/ Antiskid Functionality
Outstanding pallet stability for bulk packs.
02
Superior Matte Dispersion
Adding understated elegance to branding.
03
Fine Printability
Superior halftone dot transfer quality.
04
Good Machinability
Excellent Machinability.
05
Good Sealablity
Excellent sealing Properties.
PROPERTIES
TEST METHOD (ASTM)
UNIT
TYPICAL VALUES
HHMHF-18
HHMHF-20
HHMHF-25
PHYSICAL
Thickness
ASTM D 374
MICRON
18
20
25
Grammage
NTM
gm/m²
15.7
17.4
21.8
Yield
NTM
m²/kg
63.7
57.5
46.0
Thickness variation
%(±)
3
3
3
SURFACE
Treatment Level (min)
ASTM D 2578
dyne/cm
38
38
38
OPTICAL
Haze
ASTM D 1003
%
70-75
70-75
70-75
Gloss
Glossy
Matte
ASTM D 2457
50-52
50-52
50-52
10-13
10-13
10-13
MECHANICAL
Coefficient Of Friction
ASTM D 1894
Static
Kinetic
0.62-0.65
0.62-0.65
0.62-0.65
0.55-0.60
0.55-0.60
0.55-0.60
Tensile Strength
MD
TD
ASTM D 882
kg/cm²
≥ 1100
≥ 1100
≥ 2200
≥ 2200
≥ 2200
Modulus
MD
TD
ASTM D 882
kg/cm²
≥ 14000
≥ 14000
≥ 14000
≥ 24000
≥ 24000
≥ 24000
Elongation
MD
TD
ASTM D 882
%
140-180
140-180
140-180
40-80
40-80
40-80
THERMAL
Shrinkage at 120°C/5min
MD
TD
ASTM D 1204
%
2.0-4.0
2.0-4.0
2.0-4.0
1.0-3.0
1.0-3.0
1.0-3.0
Seal Initiation Temperature (Max)
NTM
°C
112-115
112-115
112-115
Sealing Strength (min) at 120ºC/2Bar
NTM
gms/25mm
250-350
250-350
250-350
BARRIER
Water Vapour Transmission Rate
ASTM F 1249
gm/m²/24h
8.0
8.0
7.2
Oxygen Gas Transmission Rate
ASTM D 3985
cc/m²/24h
1900
1900
1800
STORAGE & HANDLING
NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. Material should be use before 3 months from dispatch
FOOD CONTACT
NAHAROPP™ Follow with EU and FDA regulations. MSDS are available on customer request.
DISCLAIMER
The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its
own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor
accept any responsibility for the fitness of the product for any other use. Post-consumer recycled material is not used.
NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION