150x50
 

Lamination Film

HMS3

ONE SIDE METALLISED AND BOTH SIDE CORONA TREATED FILM
 
tds

VACUUM DEPOSITED ALUMINIUM LAYER

METAL RECEPTIVE LAYER

MODIFIED INNER LAYER

OPP CORE LAYER

MODIFIED INNER LAYER

NON HS TREATED LAYER

t6s
Description

 ONE SIDE METALLISED AND BOTH SIDE CORONA TREATED FILM
Features
  • Improved metal adhesion
  • Excellent machinability
  • Good lamination bond with other substrates e.g (PE, PP, PET)
  • Outstanding metal appearance
  • Good moisture & oxygen barrier
Application

  • For Sandwhich Lamination.
  • As a lamination for chocolates, biscuits & multilayer sachets etc.
THE BIG DIFFERENTIATORS

01

Excellent Sandwich Bond

Better performance on high speed.

02

Excellent lamination bond

Good lamination bond with other substrates e.g (PE, PP, PET)

03

Good Metal Bond & Metal Cracking Resistance

Durability & sustainability of barrier under extreme conditions. Enhanced extrusion/adhesive bond strengths.

04

Good Barrier Values

Improves shelf life of chips/snacks by 10% retaining natural freshness & crispness.
PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
HMS3-15 HMS3-18 HMS3-20 HMS3-25
PHYSICAL
Thickness ASTM D 374 MICRON
15 18 20 25
Grammage NTM gm/m²
13.65 16.4 18.2 22.8
Yield NTM m²/kg
73.3 61.0 55.0 44.0
Thickness variation %(±) 3
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm 38
OPTICAL
OPTICAL DENSITY
NTM

%

2.0-2.2
MECHANICAL
Coefficient Of Friction ASTM D 1894

Static

Kinetic

0.40-0.45

0.35-0.40
Tensile Strength

MD

TD
ASTM D 882

kg/cm²

1200-1500

2500-2800
Modulus

MD

TD
ASTM D 882

kg/cm²

16000-18000

26000-28000
Elongation

MD

TD
ASTM D 882

%

140-180

40-60
THERMAL
Shrinkage at 120°C/5min

MD

TD
ASTM D 1204

%

2.0-5.0

1.0-3.0
BARRIER
Water Vapour Transmission Rate ASTM F 1249 gm/m²/24h
≥ 0.6 ≥ 0.5 ≥ 0.5 ≥ 0.4
Oxygen Gas Transmission Rate ASTM D 3985 cc/m²/24h
≥ 60 ≥ 60 ≥ 60 ≥ 50
STORAGE & HANDLING

NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. material should be use before 3 months from dispatch
FOOD CONTACT

NAHAROPP™ Follow with EC and FDA regulations. MSDS are available on customer request.
DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION

Updated on : 15 May 2025