Lamination Film

MLOA

ONE SIDE METALLISED OTHER SIDE LOW HEAT SEALABLE, HIGH BARRIER FILM
 
tds

HIGH BARRIER METALLISED LAYER

METAL RECEPTIVE LAYER

INTER LAYER

OPP CORE LAYER

INTER LAYER

UNTREATED HEAT SEALABLE LAYER

t6s
Description

 ONE SIDE METALLISED OTHER SIDE LOW HEAT SEALABLE, HIGH BARRIER FILM
Features
  • Outstanding metal appearance.
  • Excellent metal adhesion.
  • Very good barrier property.
  • Broad Seal range.
  • Very good Heat seal strength.
Application

 Packaging & conversion
THE BIG DIFFERENTIATORS

01

Excellent OTR & WVTR

Improves shelf life of chips, snacks & confectionary. Very good barrier to moisture & Light.

02

Extended Seal Functionality

Very low SIT, Excellent HOT- TACK & heat Seal Strength.

03

Exceptional Metal Gloss

Very Good Graphics & Images.

04

Optimal COF

Excellent runnability at high speed m/c & lamination process.

05

Good Metal Bond.

Enhanced metal bond strength as compared normal metallised film.
PROPERTIES TEST METHOD (ASTM) UNIT TYPICAL VALUES
MLOA-15 MLOA-17 MLOA-18 MLOA-20 MLOA-25
PHYSICAL
Thickness ASTM D 374 MICRON
15 17 18 20 25
Grammage NTM gm/m²
13.65 15.47 16.40 18.20 22.80
Yield NTM m²/kg
73.3 64.6 61.0 55.0 44.0
Thickness variation %(±)
3 3 3 3 3
SURFACE
Treatment Level (min) ASTM D 2578 dyne/cm
38 38 38 38 38
OPTICAL
OPTICAL DENSITY
NTM

-
2.0-2.2 2.0-2.2 2.0-2.2 2.0-2.2 2.0-2.2
MECHANICAL
Coefficient Of Friction ASTM D 1894

Static

Kinetic
0.40-0.45 0.40-0.45 0.40-0.45 0.40-0.45 0.40-0.45
0.35-0.40 0.35-0.40 0.35-0.40 0.35-0.40 0.35-0.40
Tensile Strength

MD

TD
ASTM D 882

kg/cm²
≥ 1200 ≥ 1200 ≥ 1200 ≥ 1200 ≥ 1200
≥ 2600 ≥ 2600 ≥ 2600 ≥ 2600 ≥ 2600
Modulus

MD

TD
ASTM D 882

kg/cm²
≥ 16000 ≥ 16000 ≥ 16000 ≥ 16000 ≥ 16000
≥ 26000 ≥ 26000 ≥ 26000 ≥ 26000 ≥ 26000
Elongation

MD

TD
ASTM D 882

%
140-160 140-160 140-160 140-160 140-160
40-80 40-80 40-80 40-80 40-80
THERMAL
Shrinkage at 120°C/5min

MD

TD
ASTM D 1204

%
2.0-4.0 2.0-4.0 2.0-4.0 2.0-4.0 2.0-4.0
1.0-3.0 1.0-3.0 1.0-3.0 1.0-3.0 1.0-3.0
Seal Initiation Temperature (Max)

NTM

°C
105 105 105 105 105
Sealing Strength (min) at 120ºC/2Bar

NTM

gms/25mm
400 400 400 400 400
BARRIER
Water Vapour Transmission Rate ASTM F 1249 gm/m²/24h
≥ 0.20 ≥ 0.20 ≥ 0.20 ≥ 0.20 ≥ 0.20
Oxygen Gas Transmission Rate ASTM D 3985 cc/m²/24h
≥ 30 ≥ 30 ≥ 30 ≥ 30 ≥ 30
STORAGE & HANDLING

NAHAROPP™ does not require special storage conditions. it is recommended to storage below 30°C in order to avoid any deterioration of the film surface properties. it is advisable to use the material on FIFO basis. The film should be kept at operating environment for 24 hours before processing. material should be use before 3 months from dispatch
FOOD CONTACT

NAHAROPP™ Follow with EU and FDA regulations. MSDS are available on customer request.
DISCLAIMER

The values given in this technical datasheet are typical performance data and are believed to be accurate .These are given in good faith but it is for the customer to satisfy of the suitability for its own particular purpose. NAHAR POLY FILMS LTD. Suggests to the customer to confirm these values and product compatibility prior to their use and the company offers neither guarantee nor accept any responsibility for the fitness of the product for any other use. Post-consumer recycled material is not used.

NTM: NAHAR TEST METHOD, MD : MACHINE DIRECTION ,TD : TRANSVERSE DIRECTION